BOPP Anti-Scratch Matt Film – Keyful BOPP-SAS-M
-이축 연신 공정을 사용하여 단일 소재 폴리프로필렌으로 제작되었습니다.
-인쇄성: -안정적인 표면 장력. 플 렉소, 그라비어, 오프셋, 스크린 및 UV 인쇄와 호환됩니다. 프리미엄 핫 포일 스탬핑을 지원하여 정교하고 고급스러운 미관을 구현합니다.
•Functionality: Inherent anti-static properties and excellent resistance to oils and grease; features superior scratch and abrasion resistance (withstands 1,000 cycles at 4 lbs load）
•Superior surface performance: matte finish with a crystal-spot-free surface; matte levels of 4–5 GU or 10–12 GU available.
•After lamination, the product exhibits deep, sophisticated colors with an elegant and luxurious appearance.
This BOPP anti-scratch matte film is suitable for printing houses, gift box factories, and high-end FMCG packaging companies. It goes beyond just a “matte appearance” and delivers end-user value through controllable processing: a precise thickness of 18±2μm ensures clean die-cutting without fraying; differentiated bi-directional mechanical properties (MD 105 / TD 200 MN/m²) are suitable for complex box folding; a non-laminated surface of >38 dyne/cm ensures 100% wetting with PUR/solvent adhesives, preventing white edges and delamination; a low dynamic friction coefficient of 0.23 supports high-speed lamination without downtime; and full ASTM/GB/DIN certifications cover pharmaceutical packaging-grade compliance requirements. We provide verifiable process interfaces for your hot stamping line speed, adhesive system, and storage temperature/humidity – customization delivers certainty.
당사는 유연하고 친환경적이며 생분해성인 다양한 포장 필름의 연구 개발, 생산, 제조 및 공급에 주력하고 있으며, BOPP, BOPET, BOPA, PE 및 재활용 가능한 단일 재료 필름을 포함하여 시장의 다양한 포장 솔루션 요구를 충족시키기 위해 최선을 다하고 있습니다.
Keyful BOPP anti-scratch matte film is manufactured using a simultaneous biaxially oriented stretching process, with a stable thickness controlled at 18±2 μm (DIN 53370), balancing stiffness and winding tension adaptability. Its longitudinal/transverse tensile strength reaches 105 MN/m² and 200 MN/m² respectively (ASTM D882), with an MD/TD elongation at break of 160%/55%, and a low heat shrinkage rate of 2.7%/1.8% (100℃/10min, ASTM D1204), ensuring long-term flatness, no edge curling, and no blistering after lamination.
The surface undergoes gradient corona and micro-structure roughening composite treatment, achieving a non-laminating surface of >38 dyne/cm and a laminating surface of >36 dyne/cm (GB/T 14216), compatible with water-based adhesives, PUR, and EVA hot melt adhesives. It has a dynamic friction coefficient of 0.23–0.29 (ASTM D1894), ensuring smooth running without sticking. With a measured abrasion resistance of 4 lb/1000 cycles (ASTM D4060) + 4–5 GU low gloss + <10% haze (ASTM D2457), it delivers a delicate tactile feel, scratch and abrasion resistance, and visually subdued appearance.
애플리케이션
- 종이-플라스틱 라미네이션 산업: 고급 선물 상자, 접이식 상자, 쇼핑백, 서적 및 다양한 제품 포장용 라미네이션.
- 라벨 산업: 다양한 접착제와 호환되는 인쇄 가능한 라벨, 맞춤형 접착력을 제공합니다.
기술적 속성(일반값)
| 속성 | 단위 | 결과 | 테스트 방법 |
|---|---|---|---|
| 두께 | 미크론 | 18±2 | DIN 53 370 |
| 인장 강도 MD/TD | MN/m² | 105 | ASTM D 882 |
| 200 | |||
| 연신율 MD/TD | % | 160 | ASTM D 882 |
| 55 | |||
| 열 수축 MD/TD | % | 2.7 | ASTM D1204 100°C/10분 |
| 1.8 | |||
| Coefficient of friction (film to film) | / | 0.23 | ASTM D 1894 |
| 0.29 | |||
| Wear Resistance | / | 4 LB 1000 times | ASTM D4060 |
| 광학: 광택 헤이즈(광각) | GU | 4~5 | ASTM D2457 60°C |
| 표면 습윤 장력 적층면 |
다인/cm | >36 | GB/T 14216 |
| 표면 습윤 장력 비적층면 |
다인/cm | >38 | GB/T 14216 |
모든 속성은 표준 실험실 조건에서 테스트되었습니다: 23±2ºC; 50±5% RH, 별도 명시되지 않는 한. 해당되는 경우, 테스트는 국제 테스트 표준을 기반으로 합니다. 금속화는 하청업체에서 수행합니다. MD - 기계 방향 TD - 가로 방향.