BOPP Anti-Scratch Matt Film – Keyful BOPP-SAS-M
-Fabricado a partir de un polipropileno monomaterial mediante un proceso de estiramiento biaxial.
-Imprimibilidad: Tensión superficial estable. Compatible con flexografía, huecograbado, offset, serigrafía e impresión UV. Admite estampación en caliente de alta calidad para ofrecer una estética sofisticada y de gama alta.
•Functionality: Inherent anti-static properties and excellent resistance to oils and grease; features superior scratch and abrasion resistance (withstands 1,000 cycles at 4 lbs load）
•Superior surface performance: matte finish with a crystal-spot-free surface; matte levels of 4–5 GU or 10–12 GU available.
•After lamination, the product exhibits deep, sophisticated colors with an elegant and luxurious appearance.
This BOPP anti-scratch matte film is suitable for printing houses, gift box factories, and high-end FMCG packaging companies. It goes beyond just a “matte appearance” and delivers end-user value through controllable processing: a precise thickness of 18±2μm ensures clean die-cutting without fraying; differentiated bi-directional mechanical properties (MD 105 / TD 200 MN/m²) are suitable for complex box folding; a non-laminated surface of >38 dyne/cm ensures 100% wetting with PUR/solvent adhesives, preventing white edges and delamination; a low dynamic friction coefficient of 0.23 supports high-speed lamination without downtime; and full ASTM/GB/DIN certifications cover pharmaceutical packaging-grade compliance requirements. We provide verifiable process interfaces for your hot stamping line speed, adhesive system, and storage temperature/humidity – customization delivers certainty.
Nos centramos en la investigación y el desarrollo, la producción, la fabricación y el suministro de diversos films de envasado flexibles, ecológicos y biodegradables, que abarcan BOPP, BOPET, BOPA, PE y films monomateriales reciclables, y nos comprometemos a satisfacer las diversas necesidades de soluciones de envasado del mercado.
Keyful BOPP anti-scratch matte film is manufactured using a simultaneous biaxially oriented stretching process, with a stable thickness controlled at 18±2 μm (DIN 53370), balancing stiffness and winding tension adaptability. Its longitudinal/transverse tensile strength reaches 105 MN/m² and 200 MN/m² respectively (ASTM D882), with an MD/TD elongation at break of 160%/55%, and a low heat shrinkage rate of 2.7%/1.8% (100℃/10min, ASTM D1204), ensuring long-term flatness, no edge curling, and no blistering after lamination.
The surface undergoes gradient corona and micro-structure roughening composite treatment, achieving a non-laminating surface of >38 dyne/cm and a laminating surface of >36 dyne/cm (GB/T 14216), compatible with water-based adhesives, PUR, and EVA hot melt adhesives. It has a dynamic friction coefficient of 0.23–0.29 (ASTM D1894), ensuring smooth running without sticking. With a measured abrasion resistance of 4 lb/1000 cycles (ASTM D4060) + 4–5 GU low gloss + <10% haze (ASTM D2457), it delivers a delicate tactile feel, scratch and abrasion resistance, and visually subdued appearance.
Aplicaciones
- Industria del laminado de papel y plástico: Laminación para cajas de regalo de lujo, cajas plegables, bolsas de la compra, libros y diversos envases de productos.
- Industria de etiquetas: Etiquetas imprimibles, compatibles con diversos adhesivos, con adhesión personalizable.
Propiedades técnicas (valores típicos)
| Propiedad | Unidad | Resultado | Método de ensayo |
|---|---|---|---|
| Espesor | micras | 18±2 | DIN 53 370 |
| Resistencia a la tracción MD/TD | MN/m² | 105 | ASTM D 882 |
| 200 | |||
| Alargamiento a la rotura MD/TD | % | 160 | ASTM D 882 |
| 55 | |||
| Contracción por calor MD/TD | % | 2.7 | ASTM D1204 100°C / 10 min |
| 1.8 | |||
| Coefficient of friction (film to film) | / | 0.23 | ASTM D 1894 |
| 0.29 | |||
| Wear Resistance | / | 4 LB 1000 times | ASTM D4060 |
| Óptica: Brillo (gran angular) | GU | 4~5 | ASTM D2457 60°C |
| Tensión de humectación superficial Lado laminado |
dina/cm | >36 | GB/T 14216 |
| Tensión de humectación superficial Lado no laminado |
dina/cm | >38 | GB/T 14216 |
Todas las propiedades se prueban en condiciones estándar de laboratorio: 23±2ºC; 50±5% HR, salvo que se indique lo contrario. Cuando procede, las pruebas se basan en normas internacionales. La metalización corre a cargo de un subcontratista. MD - Dirección de la máquina TD - Dirección transversal.