BOPP Anti-Finger&Scratch&Soft Touch Matt Film -Keyful BOPP-DF
•ผลิตจากโพลีโพรพิลีนชนิดเดียวโดยใช้กระบวนการยืดสองทิศทาง.
•การพิมพ์: ความตึงผิวที่เสถียร. สามารถใช้ได้กับระบบพิมพ์ Flexo, Gravure, Offset, Screen, และ UV. รองรับการพิมพ์ฟอยล์ร้อนแบบพรีเมียมเพื่อมอบความสวยงามที่หรูหราและทันสมัย.
•Excellent barrier properties: resistant to moisture, water, and oxidation, with fold resistance .
•Functionality: Inherent anti-static properties and excellent resistance to oils and grease.
•Unique functional properties: antistatic, oil- and grease resistant, with excellent scratch and abrasion resistance (2 lbs, 200 cycles)
•Special delicate velvety or leather-like texture; matte level 2–3
•Excellent color rendering; prints remain vivid yet soft after lamination
Keyful BOPP-DF solves the “impossible triangle” of high-end packaging lamination: it must be fingerprint-resistant and leave no marks, scratch-resistant and show no damage, and have a velvet-like tactile feel. It achieves the integration of these three physical functions with a single-material PP base and a nano-micro-rough structure, rather than relying on multi-layer coating. The 18±2μm thickness ensures sharp die-cutting, the 75/126 MN/m² differential strength is suitable for deep folding of rigid boxes, and the >38 dyne/cm non-laminated surface allows 100% PUR glue wetting without white edges. We deliver not just “a roll of multi-functional film,” but a “Three-Proof Lamination Process Package” that can be integrated into your SOP: including a hot stamping temperature window chart, a recommended list of die-cutting tools, and free on-site support for your first order–ensuring that your premium pricing power truly comes from reproducible certainty on your production line.
เราให้ความสำคัญกับการวิจัยและพัฒนา การผลิต การผลิต และการจัดหาฟิล์มบรรจุภัณฑ์ที่ยืดหยุ่น เป็นมิตรต่อสิ่งแวดล้อม และย่อยสลายได้หลากหลายประเภท ครอบคลุม BOPP, BOPET, BOPA, PE และฟิล์มวัสดุเดียวที่สามารถรีไซเคิลได้ และมุ่งมั่นที่จะตอบสนองความต้องการด้านโซลูชันบรรจุภัณฑ์ที่หลากหลายของตลาด.
Keyful BOPP-DF is based on single-material PP simultaneous biaxial stretching, with a thickness of 18±2 μm (DIN 53370), MD/TD tensile strength of 75/126 MN/m², and a low heat shrinkage rate of only MD 1%/TD 0.5% (ASTM D1204). It allows for deep-crease box die-cutting without cracking or lifting. The surface utilizes a dual-gradient corona treatment + nano-micro-roughness coupling process, resulting in a non-laminated surface tension >38 dyne/cm, ensuring 100% wetting of PUR adhesives – truly achieving a “fingerprint-resistant, scratch-resistant, soft-touch” trifecta through physical properties, not coating layers. Therefore, scratch resistance passes the 2 lb/200 cycle ASTM D4060 test (scratch depth <0.8μm).
Its matte level is consistently maintained at 2–3 GU (ASTM D2457), and the velvety feel originates from structured micro-protrusions rather than the migration of slip agents, providing a touch akin to fine lambskin. The coefficient of kinetic friction is 0.23–0.29 (ASTM D1894), ensuring no slippage during high-speed lamination. An elongation at break of 148%/46% guarantees zero micro-cracking at the scoring lines of folding boxes – making it one of the few industrial-grade solutions among anti-fingerprint anti-scratch BOPP manufacturers capable of simultaneously delivering “end-product luxury” and “production line certainty.”
การประยุกต์ใช้
- อุตสาหกรรมการเคลือบกระดาษ-พลาสติก: การเคลือบสำหรับกล่องของขวัญหรูหรา, กล่องกระดาษพับ, ถุงช้อปปิ้ง, หนังสือ, และบรรจุภัณฑ์ผลิตภัณฑ์ต่างๆ.
- อุตสาหกรรมฉลาก: ฉลากที่พิมพ์ได้, เข้ากันได้กับกาวหลากหลายชนิด, สามารถปรับความยึดติดได้.
- อุตสาหกรรมบรรจุภัณฑ์ที่ยืดหยุ่น: วัสดุพิมพ์พื้นผิวสำหรับบรรจุภัณฑ์แบบหลายถุง.
คุณสมบัติทางเทคนิค (ค่าทั่วไป)
| ทรัพย์สิน | หน่วย | ผลลัพธ์ | วิธีการทดสอบ |
|---|---|---|---|
| ความหนา | ไมครอน | 18±2 | DIN 53 370 |
| ความต้านทานแรงดึง ทิศทางตามยาว/ขวาง | ตารางเมตรต่อเมตร (ตารางเมตรต่อตารางเมตร) | 75 | ASTM D 882 |
| 126 | |||
| การยืดตัวขณะขาดในแนว MD/TD | % | 148 | ASTM D 882 |
| 46 | |||
| การหดตัวด้วยความร้อนตามแนวแกน (MD) และตามแนวขวาง (TD) | % | 1 | ASTM D1204 100°C / 10 นาที |
| 0.5 | |||
| สัมประสิทธิ์แรงเสียดทาน (ระหว่างฟิล์มกับฟิล์ม) | / | 0.23 | ASTM D 1894 |
| 0.29 | |||
| ออปติคอล: ความมันวาวและความขุ่น (มุมกว้าง) | GU | 2~3 | ASTM D2457 60°C |
| แรงตึงผิวการเปียก Laminated Side / Non-Laminated Side |
ไดน์/เซนติเมตร | 36 / 38 | GB/T 14216 |
| ความต้านทานการสึกหรอ | / | 2 LB 200 times | ASTM D4060 |
คุณสมบัติทั้งหมดได้รับการทดสอบภายใต้สภาวะห้องปฏิบัติการมาตรฐาน: 23±2ºC; 50±5% RH เว้นแต่จะระบุไว้เป็นอย่างอื่น ในกรณีที่เกี่ยวข้อง การทดสอบจะอ้างอิงตามมาตรฐานการทดสอบสากล การเคลือบโลหะดำเนินการโดยผู้รับเหมาช่วง MD – ทิศทางตามเครื่อง TD – ทิศทางขวาง.