BOPP Anti-Finger&Scratch&Soft Touch Matt Film -Keyful BOPP-DF
-Изготовлен из однокомпонентного полипропилена с использованием процесса двухосного растяжения.
-Печатаемость: Стабильное поверхностное натяжение. Совместима с флексографией, глубокой, офсетной, трафаретной и УФ-печатью. Поддерживает горячее тиснение фольгой премиум-класса для придания изысканного эстетического вида.
•Excellent barrier properties: resistant to moisture, water, and oxidation, with fold resistance .
•Functionality: Inherent anti-static properties and excellent resistance to oils and grease.
•Unique functional properties: antistatic, oil- and grease resistant, with excellent scratch and abrasion resistance (2 lbs, 200 cycles)
•Special delicate velvety or leather-like texture; matte level 2–3
•Excellent color rendering; prints remain vivid yet soft after lamination
Keyful BOPP-DF solves the “impossible triangle” of high-end packaging lamination: it must be fingerprint-resistant and leave no marks, scratch-resistant and show no damage, and have a velvet-like tactile feel. It achieves the integration of these three physical functions with a single-material PP base and a nano-micro-rough structure, rather than relying on multi-layer coating. The 18±2μm thickness ensures sharp die-cutting, the 75/126 MN/m² differential strength is suitable for deep folding of rigid boxes, and the >38 dyne/cm non-laminated surface allows 100% PUR glue wetting without white edges. We deliver not just “a roll of multi-functional film,” but a “Three-Proof Lamination Process Package” that can be integrated into your SOP: including a hot stamping temperature window chart, a recommended list of die-cutting tools, and free on-site support for your first order–ensuring that your premium pricing power truly comes from reproducible certainty on your production line.
Мы занимаемся исследованиями и разработками, производством, изготовлением и поставкой различных гибких, экологически чистых и биоразлагаемых упаковочных пленок, включая БОПП, БОПЕТ, БОПА, ПЭ и перерабатываемые пленки из одного материала, и стремимся удовлетворить разнообразные потребности рынка в упаковочных решениях.
Keyful BOPP-DF is based on single-material PP simultaneous biaxial stretching, with a thickness of 18±2 μm (DIN 53370), MD/TD tensile strength of 75/126 MN/m², and a low heat shrinkage rate of only MD 1%/TD 0.5% (ASTM D1204). It allows for deep-crease box die-cutting without cracking or lifting. The surface utilizes a dual-gradient corona treatment + nano-micro-roughness coupling process, resulting in a non-laminated surface tension >38 dyne/cm, ensuring 100% wetting of PUR adhesives – truly achieving a “fingerprint-resistant, scratch-resistant, soft-touch” trifecta through physical properties, not coating layers. Therefore, scratch resistance passes the 2 lb/200 cycle ASTM D4060 test (scratch depth <0.8μm).
Its matte level is consistently maintained at 2–3 GU (ASTM D2457), and the velvety feel originates from structured micro-protrusions rather than the migration of slip agents, providing a touch akin to fine lambskin. The coefficient of kinetic friction is 0.23–0.29 (ASTM D1894), ensuring no slippage during high-speed lamination. An elongation at break of 148%/46% guarantees zero micro-cracking at the scoring lines of folding boxes – making it one of the few industrial-grade solutions among anti-fingerprint anti-scratch BOPP manufacturers capable of simultaneously delivering “end-product luxury” and “production line certainty.”
Приложения
- Индустрия бумажно-пластикового ламинирования: Ламинирование роскошных подарочных коробок, складных картонных коробок, сумок для покупок, книг и упаковки различных товаров.
- Этикеточная промышленность: Печатаемые этикетки, совместимые с различными клеями, с настраиваемой адгезией.
- Индустрия гибкой упаковки: материал для поверхностной печати на упаковке мультипак.
Технические свойства (типичные значения)
| Недвижимость | Единица | Результат | Метод испытания |
|---|---|---|---|
| Толщина | микроны | 18±2 | DIN 53 370 |
| Прочность на разрыв MD/TD | МН/м² | 75 | ASTM D 882 |
| 126 | |||
| Удлинение при разрыве MD/TD | % | 148 | ASTM D 882 |
| 46 | |||
| Термоусадка MD/TD | % | 1 | ASTM D1204 100°C / 10 мин |
| 0.5 | |||
| Коэффициент трения (пленка к пленке) | / | 0.23 | ASTM D 1894 |
| 0.29 | |||
| Оптические: Глянцевая дымка (широкий угол) | GU | 2~3 | ASTM D2457 60°C |
| Поверхностное смачивание Laminated Side / Non-Laminated Side |
дин/см | 36 / 38 | GB/T 14216 |
| Износостойкость | / | 2 LB 200 times | ASTM D4060 |
Все свойства проверены в стандартных лабораторных условиях: 23±2ºC; 50±5% RH, если не указано иное. Там, где это необходимо, испытания основаны на международных стандартах. Металлизация проводится субподрядчиком. MD - машинное направление TD - поперечное направление.