Cellulose Anti-Finger Soft Touch Matt Film – Keyful CP-AFST-M
Eco-Sourcing: Derived from renewable wood pulp. Certified for industrial and home composting.
Printability: Stable surface tension. Compatible with Flexo, Gravure, Offset, Screen, and UV printing. Supports premium hot foil stamping to deliver a sophisticated, high-end aesthetic.
High Barrier: Superior moisture, water, and oxygen resistance. High gloss and crease-resistant. Data
Functionality: Inherent anti-static properties and excellent resistance to oils and grease;Exquisite velvet and leather-like touch; ultra-matte finish (2-3 degrees);Excellent color fidelity; laminated prints appear vibrant yet soft.Features anti-fingerprint functionality, leaving no marks when touched.
Based on renewable wood pulp, combined with PVDC-enhanced barrier properties and an ultra-soft, tactile matte layer, it offers comprehensive advantages such as fingerprint resistance, high transparency, and low moisture absorption. It is suitable for customized high-end packaging and lamination solutions, enhancing brand quality and product durability.
We focus on the research & development, production, manufacturing, and supply of various flexible, environmentally friendly, and biodegradable packaging films, covering BOPP, BOPET, BOPA, PE, and recyclable single-material films, and are committed to meeting the diverse packaging solution needs of the market.
Keyful Cellulose Anti-Finger Soft Touch Matt Film – CP-AFST-M, derived from reclaimed wood pulp, is certified for both industrial and home composting. Optimized surface tension and microstructure provide broad compatibility with printing processes, supporting Flexo, gravure, offset, screen, and UV printing. It can also be used for high-end foil stamping and imaging, enhancing brand quality.
The material features high barrier properties, moisture and oil resistance, antistatic properties, and extremely high color fidelity. Its unique ultra-matte texture (2-3°) provides a suede-like soft touch while offering anti-fingerprint properties to maintain a clean surface. The thickness is 25±2 microns, the basis weight is 37.5±2 g/m², the tensile strength MD/TD is approximately 50/21 MN/m², the elongation at break is 16/40%, the sealing strength is 1.77 g(f)/25mm, the sealing range is 120-160°C, the oxygen permeability is 1.6 cc/m²·d, and the water vapor transmission rate is 20 g/m²·d. With a gloss/haze of 2-3 GU, it is suitable for high-end gift boxes, color boxes, handbags, book covers, and outer packaging, offering an integrated color printing-lamination solution. In single-layer packaging, labels, and laminated products, it achieves the combined value of “soft touch + high protection.”
Applications
•Flexible Packaging Industry: Surface Printing Material for Multiple Pouch Formats.
•Paper-Plastic Lamination: Premium gift boxes, color boxes, handbags, book covers, and outer packaging.
•Labeling: Printable facestock with customizable adhesive/tack levels.
Technical Properties (Typical Values)
| Property | Unit | Result | Test method |
|---|---|---|---|
| Thickness | microns | 25±2 | DIN 53 370 |
| Unit weight | g/m² | 37.5±2 | ASTM D-2673 |
| Yield | m²/kg | 26.7±2 | ASTM D-2673 |
| Tensile strength MD/TD | MN/m² | 50/21 | ASTM D 882 |
| Elongation at break MD/TD | % | 16/40 | ASTM D 882 |
| Seal strength | g(f)/25mm | 1.77 | 135°C; 0.5secs; 69kN/m² |
| Seal range | °C | 120-160 | 0.5secs; 69kN/m² |
| Coefficient of friction (film to film) | / | 0.49/0.45 | ASTM D 1894 |
| Oxygen permeability | cc/m²·d | 1.6 | ASTM-D3985 23°C / 0% R.H. |
| Water vapor permeability | g/m²·d | 20 | ASTM F1249 38°C 90% R.H. |
| Optical: Gloss Haze (wide angle) | GU | 2~3 | ASTM D2457 60°C |
All properties are tested under standard laboratory conditions: 23±2ºC; 50±5% RH, unless otherwise stated. Where relevant, tests are based on international testing standards. Metallising is conducted by a sub-contractor. MD – Machine Direction TD – Transverse Direction.