Cellulose Anti-Finger Soft Touch Matt Film – Keyful CP-AFST-M
Eco-sourcing: Afkomstig van hernieuwbare houtpulp. Gecertificeerd voor industriële en thuiscompostering.
Printbaarheid: Stabiele oppervlaktespanning. Compatibel met flexo-, diepdruk-, offset-, zeef- en UV-druk. Ondersteunt hoogwaardige hot foil stamping voor een verfijnde, high-end esthetiek.
Hoge barrière: Superior moisture, water, and oxygen resistance. High gloss and crease-resistant. Data
Functionaliteit: Inherent anti-static properties and excellent resistance to oils and grease;Exquisite velvet and leather-like touch; ultra-matte finish (2-3 degrees);Excellent color fidelity; laminated prints appear vibrant yet soft.Features anti-fingerprint functionality, leaving no marks when touched.
Based on renewable wood pulp, combined with PVDC-enhanced barrier properties and an ultra-soft, tactile matte layer, it offers comprehensive advantages such as fingerprint resistance, high transparency, and low moisture absorption. It is suitable for customized high-end packaging and lamination solutions, enhancing brand quality and product durability.
Wij richten ons op onderzoek & ontwikkeling, productie, fabricage en levering van diverse flexibele, milieuvriendelijke en biologisch afbreekbare verpakkingsfolies, waaronder BOPP, BOPET, BOPA, PE en recyclebare single-material folies, en zijn toegewijd aan het voldoen aan de diverse behoeften van de markt op het gebied van verpakkingsoplossingen.
Keyful Cellulose Anti-Finger Soft Touch Matt Film – CP-AFST-M, derived from reclaimed wood pulp, is certified for both industrial and home composting. Optimized surface tension and microstructure provide broad compatibility with printing processes, supporting Flexo, gravure, offset, screen, and UV printing. It can also be used for high-end foil stamping and imaging, enhancing brand quality.
The material features high barrier properties, moisture and oil resistance, antistatic properties, and extremely high color fidelity. Its unique ultra-matte texture (2-3°) provides a suede-like soft touch while offering anti-fingerprint properties to maintain a clean surface. The thickness is 25±2 microns, the basis weight is 37.5±2 g/m², the tensile strength MD/TD is approximately 50/21 MN/m², the elongation at break is 16/40%, the sealing strength is 1.77 g(f)/25mm, the sealing range is 120-160°C, the oxygen permeability is 1.6 cc/m²·d, and the water vapor transmission rate is 20 g/m²·d. With a gloss/haze of 2-3 GU, it is suitable for high-end gift boxes, color boxes, handbags, book covers, and outer packaging, offering an integrated color printing-lamination solution. In single-layer packaging, labels, and laminated products, it achieves the combined value of “soft touch + high protection.”
Toepassingen
•Flexible Packaging Industry: Surface Printing Material for Multiple Pouch Formats.
•Papier-kunststof laminering: Premium geschenkdozen, kleurdozen, handtassen, boekomslagen en omverpakkingen.
•Label: Printable facestock with customizable adhesive/tack levels.
Technische eigenschappen (typische waarden)
| Eigendom | Eenheid | Resultaat | Testmethode |
|---|---|---|---|
| Dikte | microns | 25±2 | DIN 53 370 |
| Gewicht per eenheid | g/m² | 37.5±2 | ASTM D-2673 |
| Opbrengst | m²/kg | 26.7±2 | ASTM D-2673 |
| Treksterkte MD/TD | MN/m² | 50/21 | ASTM D 882 |
| Rek bij breuk MD/TD | % | 16/40 | ASTM D 882 |
| Sterkte afdichting | g(f)/25mm | 1.77 | 135°C; 0,5secs; 69kN/m² |
| Afdichtingsbereik | °C | 120-160 | 0,5secs; 69kN/m² |
| Wrijvingscoëfficiënt (film tot film) | / | 0.49/0.45 | ASTM D 1894 |
| Zuurstofdoorlaatbaarheid | cc/m²-d | 1.6 | ASTM-D3985 23°C / 0% R.H. |
| Waterdampdoorlaatbaarheid | g/m²-d | 20 | ASTM F1249 38°C 90% R.H. |
| Optisch: Glans Haze (groothoek) | GU | 2~3 | ASTM D2457 60°C |
Alle eigenschappen zijn getest onder standaard laboratoriumomstandigheden: 23±2ºC; 50±5% RH, tenzij anders vermeld. Waar relevant zijn de testen gebaseerd op internationale teststandaarden. Het metalliseren wordt uitgevoerd door een onderaannemer. MD - Machinerichting TD - Dwarsrichting.