Матовая пленка BOPP Anti-Finger Soft Touch - Keyful BOPP-AFST-M
-Изготовлен из однокомпонентного полипропилена с использованием процесса двухосного растяжения.
-Печатаемость: Стабильное поверхностное натяжение. Совместима с флексографией, глубокой, офсетной, трафаретной и УФ-печатью. Поддерживает горячее тиснение фольгой премиум-класса для придания изысканного эстетического вида.
•Excellent barrier properties: resistant to moisture, water, and oxidation, with fold resistance .
•Functionality: Inherent anti-static properties and excellent resistance to oils and grease.
•Soft, velvety, and smooth texture with delicate feel; matte level 2-3
•Excellent color rendering; prints remain vivid yet soft after lamination
•Fingerprint-resistant; touch leaves no marks
Keyful BOPP-AFST-M is not “ordinary matte film with a tactile agent added,” but a closed-loop product based on single-material PP, manufactured through simultaneous stretching + dual-gradient corona treatment + nano-micro-roughening. It allows luxury packaging to maintain an ultra-matte finish of 1–2 GU while completely solving the three major delivery issues of fingerprint retention, hot stamping collapse, and die-cutting burrs. Its 75/126 MN/m² differentiated strength is suitable for deep folding of folding boxes and load-bearing of shopping bags. The >38 dyne/cm non-laminated surface ensures 100% PUR glue wetting, eliminating white edges. We deliver not just a roll of film, but a “soft-touch consistency process package” reproducible on your production line – including a parameter card, glue window diagram, die-cutting tool recommendations, and free on-site production assistance for your first order.
Мы занимаемся исследованиями и разработками, производством, изготовлением и поставкой различных гибких, экологически чистых и биоразлагаемых упаковочных пленок, включая БОПП, БОПЕТ, БОПА, ПЭ и перерабатываемые пленки из одного материала, и стремимся удовлетворить разнообразные потребности рынка в упаковочных решениях.
Keyful BOPP-AFST-M utilizes a single-material PP simultaneous biaxial stretching process, with a thickness of 18±2 μm (DIN 53370), MD/TD tensile strength of 75/126 MN/m², and a low heat shrinkage rate of only MD 1%/TD 0.5% (100℃/10min). After lamination, it ensures sharp, non-whitening creases on boxes. The surface undergoes dual-gradient corona treatment, with the non-laminated side exceeding 38 dyne/cm, offering full compatibility with Flexo/Gravure/UV printing and high-precision hot stamping – truly achieving “soft touch without sacrificing print sharpness.”
It’s velvet matte finish (1–2 GU) originates from a nano-scale micro-rough structure, a non-coated physical construction, resulting in fingerprint resistance, a silky touch, oil resistance, and anti-static properties. The coefficient of kinetic friction is 0.23–0.29 (ASTM D1894), ensuring smooth running on machines without slippage. A breaking elongation of 148%/46% guarantees that deep-drawn boxes will not break during die-cutting, making it a process-controllable representative of high-end BOPP anti-fingerprint soft touch BOPP film.
Приложения
- Индустрия бумажно-пластикового ламинирования: Ламинирование роскошных подарочных коробок, складных картонных коробок, сумок для покупок, книг и упаковки различных товаров.
- Этикеточная промышленность: Печатаемые этикетки, совместимые с различными клеями, с настраиваемой адгезией.
- Индустрия гибкой упаковки: материал для поверхностной печати на упаковке мультипак.
Технические свойства (типичные значения)
| Недвижимость | Единица | Результат | Метод испытания |
|---|---|---|---|
| Толщина | микроны | 18±2 | DIN 53 370 |
| Прочность на разрыв MD/TD | МН/м² | 75 | ASTM D 882 |
| 126 | |||
| Удлинение при разрыве MD/TD | % | 148 | ASTM D 882 |
| 46 | |||
| Термоусадка MD/TD | % | 1 | ASTM D1204 100°C / 10 мин |
| 0.5 | |||
| Коэффициент трения (пленка к пленке) | / | 0.23 | ASTM D 1894 |
| 0.29 | |||
| Оптические: Глянцевая дымка (широкий угол) | GU | 1~2 | ASTM D2457 60°C |
| Поверхностное смачивание Ламинированная сторона |
дин/см | >36 | GB/T 14216 |
| Поверхностное смачивание Неламинированная сторона |
дин/см | >38 | GB/T 14216 |
Все свойства проверены в стандартных лабораторных условиях: 23±2ºC; 50±5% RH, если не указано иное. Там, где это необходимо, испытания основаны на международных стандартах. Металлизация проводится субподрядчиком. MD - машинное направление TD - поперечное направление.