Cellulose High-Barrier Label Film - Keyful CP-BL
Cellulose High-Barrier Label Film - Keyful CP-BL
Cellulose High-Barrier Label Film - Keyful CP-BL
Cellulose High-Barrier Label Film - Keyful CP-BL
Cellulose High-Barrier Label Film - Keyful CP-BL
Cellulose High-Barrier Label Film - Keyful CP-BL

Cellulose High-Barrier Label Film – Keyful CP-BL

•Eco-Sourcing: Derived from renewable wood pulp. Certified for industrial and home composting.

•No shrinkage, no deformation, Compatible with oil based or water-based adhesives, release papers, or release films.

•Adhesion can be customized.

•Printable, resistant to alcohol and abrasion.

•High strength, excellent toughness, high transparency, and strong tear resistance.

This film achieves a comprehensive performance of high strength and toughness, transparency, alcohol resistance, and abrasion resistance through the combination of cellulose high barrier and compostable certification. It also offers customizable adhesion, thickness, and printability, helping wholesale customers achieve “eco-friendly + high-performance + customized” label solutions.

We focus on the research & development, production, manufacturing, and supply of various flexible, environmentally friendly, and biodegradable packaging films, covering BOPP, BOPET, BOPA, PE, and recyclable single-material films, and are committed to meeting the diverse packaging solution needs of the market.

High-performance cellulose high-barrier label film, derived from renewable wood pulp, offers excellent alcohol resistance, abrasion resistance, and high transparency. This film exhibits no shrinkage or deformation and is compatible with both oil-based and water-based adhesives, as well as release paper/film systems.

Adhesion is customizable to meet diverse processing needs. It holds industrial and home composting certifications, supports sustainable recycling and green production, and is suitable for various applications in the label industry, including security labels, sealing labels, and wine labels. This film belongs to the cellulose high-barrier film series, an Eco high-end high-barrier packaging film, combining high strength, excellent toughness, and traceable environmental attributes, ensuring stable performance in high-viscosity printing, alcohol resistance, and long-term durability.

Applications

Label Industry: Various security labels, seal labels, wine labels, and consumer goods labels.

Application Scenarios: Enhances anti-counterfeiting and environmental resistance for various security labels, seal labels, wine labels, and consumer product labels in the Label Industry.

Applicable Processes: Compatible with various printing processes, suitable for water-based/solvent-based ink printing and subsequent lamination, ensuring vibrant colors and stable interlayer adhesion.

Supply Chain Advantages: Offers customized adhesion, thickness, and appearance parameters in bulk, quickly responding to OEM/ODM needs and reducing process adjustment costs for downstream factories.

Technical Properties (Typical Values)

Property Unit Result Test method
Thickness microns 23±2 DIN 53 370
Unit weight g/m² 35±2 ASTM D-2673
Yield m²/kg 28.6±2 ASTM D-2673
Tensile strength MD/TD MN/m² 50 ASTM D 882
21
Elongation at break MD/TD % 16 ASTM D 882
40
Seal strength g(f)/25mm 1.77 135°C; 0.5secs; 69kN/m²
Seal range °C 120-160 0.5secs; 69kN/m²
Coefficient of friction (film to film) / 0.49 / 0.45 ASTM D 1894
Oxygen permeability cc/m²·d 3 ASTM D3985 23°C / 0% R.H.
Water vapor permeability g/m²·d 16 ASTM F1249 38°C 90% R.H.

All properties are tested under standard laboratory conditions: 23±2ºC; 50±5% RH, unless otherwise stated. Where relevant, tests are based on international testing standards. Metallising is conducted by a sub-contractor. MD – Machine Direction TD – Transverse Direction.

    Name*

    Email*

    Phone

    Country

    Company Name

    Subject

    Message*

    * Required

    Suitable for normal and medium-high temperature environments. The specific temperature resistance range needs to be determined according to the actual adhesive and printing process, but it usually covers the temperature requirements of common label usage scenarios.

    Compatible with solvent-based and water-based adhesives, as well as common release paper/release film. Specific adhesion and peel force curves need to be confirmed through lamination testing.

    Yes, the film surface and printing system have been optimized to provide good adhesion and imaging effects with water-based inks, making it suitable for environmentally friendly printing processes.

    Customizable parameters can be provided based on application scenarios (e.g., low/medium/high adhesion). Formulas and coating thicknesses can be verified before mass production.

    We can provide corresponding certification documents and test reports to ensure compliance with industrial and home composting standards.

    The MOQ depends on the specifications and customized parameters. We usually accept both medium-volume pilot production and mass production schemes to facilitate phased volume increases for customers.

    From sample confirmation to mass production, the typical cycle is based on specifications and production line scheduling. Customized requirements may slightly extend the lead time.

    We provide packaging solutions suitable for cartons and pallets, with moisture-proof and damage-resistant designs to ensure complete arrival.