Cellulose Glossy Film High Gloss Clear Biodegradable Compostable
Features-High Gloss & Clarity Cellulose Glossy film
Eco-Sourcing: Derived from renewable wood pulp. Certified for industrial and home composting.
Printability: Stable surface tension. Compatible with Flexo, Gravure, Offset, Screen, and UV printing. Supports premium hot foil stamping to deliver a sophisticated, high-end aesthetic.
High Barrier: Superior moisture, water, and oxygen resistance. High gloss and crease-resistant.
Functionality: Inherent anti-static properties. Excellent resistance to oils and grease.
We focus on the research & development, production, manufacturing, and supply of various flexible, environmentally friendly, and biodegradable packaging films, covering BOPP, BOPET, BOPA, PE, and recyclable single-material films, and are committed to meeting the diverse packaging solution needs of the market.
KEYFUL cellulose glossy film is made from renewable wood pulp. It has high gloss and excellent clarity and meets industrial and home composting standards. It has stable surface tension and is compatible with flexographic, contour, gravure, screen, and UV printing. It also supports high-end hot stamping processes to enhance the perceived quality of packaging. With excellent barrier properties, anti-static characteristics, oil resistance, and grease resistance, it is suitable for high-end outer packaging such as gift boxes, color boxes, and handbags, as well as a variety of products such as labels and flexible packaging.
Applications
Paper-Plastic Lamination: Premium gift boxes, color boxes, handbags, book covers, and outer packaging.
Labeling: Printable facestock with customizable adhesive/tack levels.
Flexible Packaging: High-performance surface material for multiple pouch formats.
Technical Properties (Typical Values)
| Property | Unit | Result | Test method |
|---|---|---|---|
| Thickness | microns | 23±2 | DIN 53 370 |
| Unit weight | g/m² | 35±2 | ASTM D-2673 |
| Yield | m²/kg | 28.6±2 | ASTM D-2673 |
| Tensile strength MD/TD | MN/m² | 56 28 |
ASTM D 882 |
| Elongation at break MD/TD | % | 22 70 |
ASTM D 882 |
| Elasticity modulus MD/TD | MN/m² | > 1200 > 600 |
ASTM D 882 |
| Coefficient of friction (film to film) | / | 0.49 0.45 |
ASTM D 1894 |
| Oxygen permeability | cc/m²·d | 1.6 | ASTM D3985 23°C / 0% R.H. |
| Water vapor permeability | g/m²·d | 20 | ASTM F1249 38°C 90% R.H. |
All properties are tested under standard laboratory conditions: 23±2ºC; 50±5% RH, unless otherwise stated. Where relevant, tests are based on international testing standards. Metallising is conducted by a sub-contractor. MD -Machine Direction TD – Transverse Direction